Seneste kundespørgsmål QA

Efter en periode med sortering indsamlede vi igen lidt feedback fra kunder og lavede en artikel, som alle kunne læse.

Q1: Hvorfor er din zirconia grøn efter sintring?

A1:It is because your finance has been polluted, different types of zirconia have different subsidiary substances during production. when sintering the substance will get rid of zirconia and come to the heart of finance, it made the heart of finance was polluted because the substance doesn't get rid of completely.

Pls, sinter the finance empty immediately to help the substance get rid of completely. Each time sintering the heating elements will have new crystalline film. It is better to change the sintering tray and beads as well.

Tips til at undgå forurening:

1, Forskellige typer zirconia må ikke sintres kontinuerligt.

For eksempel, sintring af hvide blokke i dag, hvis du i morgen har brug for sintrede forskyggede blokke, skal du sintre finansen tom efter hvide blokke og derefter sintre forskyggede.

2, Alle de hvide blokke skal tørre 200 grader 30 minutter før sintring

Q2: Hvad er forskellen mellem SHT Multilayer og 3D-Plus Multilayer?

A2: SHT er en farvegradient. Styrken er 1200MPA og 45 procent gennemskinnelighed.

3D-Plus er både farve- og styrkegradient. Styrke fra 600MPA til 900MPA, gennemsigtighed fra 43 procent til 49 procent.

I mellemtiden tester vi en ny 3D E-Plus, Strength kan være Max 1100 og translucens fra 47 procent til 49 procent.

Q3: Pontinebrud efter ruder?

A3: Der er to muligheder for dette problem:

1. The upper gingival porcelain requires repeated enamels, and the burned bridge undergoes multiple heating and cooling. Pulling and cracking are caused by the too fast cooling rate.
Suggestions: Lower the cooling rate and reduce the number of times porcelain loading

Porcelain furnace cooling program should be set a little slower, porcelain furnace cooling too fast will cause thermal stress, thermal shock, ceramics are most afraid of rapid cooling and heating, porcelain furnace cooling down a little bit, the lower temperature limit is set a little lower

This needs to be paid attention to in the porcelain furnace, the mouthful of rapid cold causes thermal stress cracking
Generally, the teeth in the porcelain furnace come out at 700 degree  and come into contact with the air, and the teeth at 700 degree  encounter the cold air at 25 degree , which causes cracking.
Easiest to break from the missing position, because the missing position is solid, accumulates more heat, and dissipates slowly

2. When the porcelain is cut, the teeth are cut vertically with fine slices. (In the past, metal teeth and porcelain teeth were cut in this way, so technicians are used to it).

Suggestion: When the car porcelain is cut between the teeth, it should be cut sideways in the direction of the teeth. However, this possibility is generally small.